High elasticity Molding Silicone

HIGH ELASTICITY MOLDING SILICONE DESRIPTION
         High elasticity molding silicone is a kind of room temperature vulcanized silicone rubber in condensation type. It's generally named as two part silicone rubber, Part A is a flowable liquid, part B is the curing agent or catalyst. It's mainly used for all mold making with different size and pattern.


HIGH ELASTICITY MOLDING SILICONE APPLICTION
        Two component rtv liquid silicone making mold for stone figures molding, which with good tensile strength as well as high duplication times ,so it is perfect for making mold in statue and figures industries ,such as Stone figurine ,ceramic statues,polyurethane statuary, ceramic statues,polyurethane animals,Buddha, plaster ceiling, artificial stone, GRC home decorations etc.while,it also application for making mold for Resin and poly resin crafts, ,Lighting ornaments, candles crafts, statue Buddha, relief, artifacts copied,Animals and plants sculpture.


HIGH ELASTICITY MOLDING SILICONE FEATURES
1.Suitable for both pouring molding and brushing molding

2. Strong tear strength and tensile strength

3. excellent non-stick effect 

4. Easily release air to avoid bubbles

5. Various hardness from 20 to 40 shore A

6. Excellent flexibility, easy to demould.

7.Good cut-growth resistance

8. High temperature resistance, high duplication times and repeated use



HIGH ELASTICITY MOLDING SILICONE OPERATION AND NOTES
Step 1:Prepare the original mold：Weight silicone & curing agent according to the mix  ratio recommended](100:2 to100:5),than Remember  to silicone& curing agent evenly, otherwise the silicon  rubber will be partly solidified and bring problems in  your finaloperation. What’smore, the finished moldswill  meet a short life.

All of these will cause a waste of  silicon rubber.
1.The curing rate of this product is closely relevant to the  temperature. The higher the temperature is, the greater the  humidity is and the curing speed becomesfaster.

2.Users can choose the curing agent according to the weather  condition, and adjust the amount of the curing agent in order to  reach the appropriated curing rate. 

Step 2:Vacuum pumping: Without exception, this step takes less than 10  minutes. Otherwise, it will cause cross linking  reaction, and no morefurther steps will be available.

Step 3:Pouring casting or Brushing operation 1. For simple pattern products we suggest use pouring  operation way， which will be very easy to operate and  demould. Pourable silicone requirelight viscosity which  will be easy to flow smoothly and easy to de-air .  2.For delicate pattern products we suggest use brushing  operation way，which can copy the pattern exactly .  Brushable silicone require high viscosity  which won’t be easy to flow away and easy to brush .  

Step 4:Demoulding:After 35 hours later, can  demould the silicone mold,It’s will be better for  mold to demould after 24 hours We suggest to set the silicone mold for another  24 hours after demould before put into large production .    



HIGH ELASTICITY MOLDING SILICONE SHELF LIFE
Twelve(12) months from date of shipment when stored under 25℃ in the original sealed packages at dry and cool places.  


HIGH ELASTICITY MOLDING SILICONE PACKAGE
1kg/jar, 5kgs/drum, 20kgs/drum, 25kgs/drum, 200kgs/drum and vacuumed packing is available.